Elastic blends comprising crystalline polymer and crystallizable polym

ABSTRACT

Improved thermoplastic polymer blend compositions comprising an isotactic polypropylene component and an alpha-olefin and propylene copolymer component, said copolymer comprising crystallizable alpha-olefin sequences. In a preferred embodiment, improved thermoplastic polymer blends are provided comprising from about 35% to about 85% isotactic polypropylene and from about 30% to about 70% of an ethylene and propylene copolymer, wherein said copolymer comprises isotactically crystallizable propylene sequences and is predominately propylene. The resultant blends manifest unexpected compatibility characteristics, increased tensile strength, and improved process characteristics, e.g., a single melting point.

Continuation-in-part (CIP) of prior application Ser. No.: 09/108,467 filed Jul. 1, 1998, now abandoned from which priority is claimed under 35 U.S.C. §120.

FIELD OF THE INVENTION

The invention relates to a blend of at least two thermoplastic components differing in their crystallinities. The blend has a heterogeneous morphology with distinct phase separated zones of different composition and crystallinity present. The resulting blend with the defined morphology shows dramatic improvements in mechanical deformation recoverability when compared to its individual unblended components. The invention also relates to improvements in the flexibility of the blend. Changes in the relative amounts or the crystallinities of the blend components or the morphology of the blend affect the recoverability and the flexibility of the blend.

The inventive blends designed for recoverability contains a dispersed phase of a greater crystallinity and a continuous phase of lesser crystallinity. The sizes of the individual domains of the dispersed phase are very small with the smallest length dimension for the dispersed phase being less than 5 μm. This phase size of the dispersed phase is maintained during processing even without crosslinking. The inventive blends designed for flexibility have a slightly wider range in morphology as the components of greater and lesser crystallinity can also be co-continuous. The components of the blend in both cases are also compatible to the extent that no compatibilizer needs to be added to attain and retain this fine morphology. Furthermore, this invention describes improving the mechanical deformation recoverability of the aforementioned blends by aging the blends and mechanically orienting the articles formed from these blends.

One of the components is a polymer comprising predominately stereospecific polypropylene, preferably isotactic polypropylene. This is the component with greater crystallinity. A second component is a copolymer of propylene and a C₂, C₃-C₂₀ α-olefin, preferably ethylene. This is the component with lesser crystallinity. In the copolymer the propylene is polymerized substantially stereospecifically. The copolymer has a substantially uniform composition distribution preferably as a result of polymerization with a metallocene catalyst. Most preferably, said second component is an ethylene propylene copolymer, e.g. ethylene propylene semicrystalline elastomer.

BACKGROUND OF THE INVENTION

There is a need in the art for polymeric blends having a stereospecific polypropylene component with good tensile strength while still providing suitable mechanical recoverability (elastic recovery) and flexibility (low flexural modulus). This invention is aimed at improving the aforementioned properties of blends having a stereoregular polypropylene component, especially isotactic polypropylene. This is achieved by blending the stereoregular polypropylene component with a copolymer of propylene and a C₂, C₃-C₂₀ α-olefin. This copolymer is less crystalline than the isotactic polypropylene. In the copolymer the propylene is polymerized substantially stereospecifically. Most preferably, the copolymer is an ethylene propylene copolymer, e.g., ethylene propylene thermoplastic elastomer. The copolymer has a substantially uniform composition distribution preferably as a result of polymerization with a metallocene catalyst Composition distribution is a property of copolymers indicating a statistically significant intermolecular or intramolecular difference in the composition of the polymer. Methods for measuring compositional distribution are described later.

Blends of isotactic polypropylene and ethylene propylene rubber are well known in the prior art. However, the traditional Ziegler-Natta catalysts cannot make ethylene propylene thermoplastic elastomers which simultaneously are uniform in compositional distribution, have substantially stereospecific propylene residues and have less than 35 wt. % ethylene.

U.S. Pat. No. 3,882,197 to Fritz et al. describes blends of stereoregular propylene/alpha-olefin copolymers, stereoregular propylene, and ethylene copolymer rubbers. In U.S. Pat. No. 3,888,949 Chi-Kai Shih, assigned to E I Du Pont, shows the synthesis of blend compositions containing isotactic polypropylene and copolymers of propylene and an alpha-olefin, containing between 6-20 carbon atoms, which have improved elongation and tensile strength over either the copolymer or isotactic polypropylene. Copolymers of propylene and alpha-olefin are described wherein the alpha-olefin is hexene, octene or dodecene. However, the copolymer is made with a heterogeneous titanium catalyst resulting in copolymers with non-uniform composition distribution and a broad molecular weight distribution. Non-uniform intramolecular compositional distribution is evident in U.S. Pat. No. 3,888,949 by the use of the term “block” in the description of the polymer where the copolymer is described as having “sequences of different alpha-olefin content.” Within the context of the invention described above the term sequences describes a number of olefin monomer residues linked together by chemical formed during polymerization.

In U.S. Pat. No. 4,461,872, A.C.L. Su improved on the properties of the blends described in U.S. Pat. No. 3,888,949 by using another heterogeneous catalyst system which is expected to form copolymers which have statistically significant intermolecular and intramolecular compositional differences.

In two successive publications in the journal of Macromolecules, 1989, V22, pages 3851-3866, J. W. Collette of E. I. Du Pont has described blends of isotactic polypropylene and partially atactic polypropylene which have desirable tensile elongation properties. However, the partially atactic propylene has a broad molecular weight distribution as shown in FIG. 8 of the first publication. The partially atactic polypropylene is also composed of several fractions, which differ in the level of tacticity of the propylene units as shown by the differences in the solubility in different solvents. This is shown by the corresponding physical decomposition of the blend which is separated by extraction with different solvents to yield individual components of uniform solubility characteristics as shown in Table IV of the above publications.

More recently several authors have shown the formation of more refined structures of partially atactic, partially isotactic polypropylene which have elastomeric properties. It is believed that in these components each molecule consists of portions which are isotactic and therefore crystallizable while the other portions of the same polypropylene molecule are atactic and therefore amorphous. Examples of these propylene homopolymers containing different levels of isotacticity in different portions of the molecule are described by R. Waymouth in U.S. Pat. No. 5,594,080, in the article in the Journal American Chemical Society (1995), Vol. 117, page 11586, and in the article in the Journal American Chemical Society (1997), Vol. 119, page 3635, J. Chien in the journal article in the Journal of the American Chemical Society (1991), Vol. 113, pages 8569-8570; and S. Collins in the journal article in Macromolecules (1995) Vol. 28, pages 3771-3778. These articles describe a specific polymer, but do not describe the blends with a more crystalline polymer such as isotactic polypropylene.

In U.S. Pat. Nos. 3,853,969 and 3,378,606, E. G. Kontos discloses the formation of in situ blends of isotactic polypropylene and “stereo block” copolymers of propylene and another olefin of 2 to 12 carbon atoms, including ethylene and hexene. The copolymers of this invention are necessarily heterogeneous in intermolecular and intramolecular composition distribution. This is demonstrated by the synthesis procedures of these copolymers which involve sequential injection of monomer mixtures of different compositions to synthesize polymeric portions of analogously different compositions. In addition, FIG. 1 of both patents shows that the “stereo block” character, which is intra or intermolecular compositional differences in the context of the description of the present invention, is essential to the benefit of the tensile and elongation properties of the blend. Moreover, all of these compositions either do not meet all of the desired properties for various applications, and/or involve costly and burdensome process steps to achieve the desired results.

Similar results are anticipated by R. Holzer and K. Mehnert in U.S. Pat. No. 3,262,992 assigned to Hercules wherein the authors disclose that the addition of a estereoblock copolymer of ethylene and propylene to isotactic polypropylene leads to improved mechanical properties of the blend compared to isotactic polypropylene alone. However, these benefits are described only for the stereoblock copolymers of ethylene and propylene. These copolymers were synthesized by changing the monomer concentrations in the reactor with time. This is shown in examples 1 and 2. The stereoblock character of the polymer is graphically shown in the molecular description (column 2, line 65) and contrasted with the undesirable random copolymer (column 2, line 60). The presence of stereoblock character in these polymers is shown by the high melting point of these polymers and the poor solubility in hydrocarbons at ambient temperature.

There is a need for a polyolefin blend composition which is thermally stable, heat resistant, light resistant and generally suitable for thermoplastic elastomer (TPE) applications which has advantageous processing characteristics. We have found that by blending a crystalline propylene polymer, hereinafter referred to as the “first polymer component, (FPC)” and a crystallizable propylene alpha olefin copolymer polymer, hereinafter referred to as the “second polymer component (SPC)”, advantageous processing characteristics result while still providing a composition having decreased flexural modulus and increased tensile strength, elongation, recovery and overall toughness. It is possible to have the addition of a third polymeric component which is another crystallizable propylene alpha olefin copolymer indicated as SPC2 in the text below which has crystallinity intermediate between the FPC and the, SPC. The SPC2 also has a narrow composition distribution and is made with a metallocene catalyst. The addition of SPC2 leads to a finer morphology and improvements in some of the properties of the blend of FPC and SPC.

The term “crystalline,” as used herein for FPC, characterizes those polymers which possess high degrees of inter- and intra-molecular order, and which melt higher than 110° C. and preferably higher than 115° C. and more preferably higher than 130° C. and preferably have a heat of fusion of at least 75 J/g, as determined by DSC analysis. And, the term “crystallizable,” as used herein for SPC describes polymers which are mainly amorphous in the undeformed state, but can crystalize upon stretching or annealing. Crystallization may also be initiated by the presence of a crystalline polymer such as the FPC. These polymers have a melting point of less than 105° C. or preferably less than 100° C. and preferably have a heat of fusion of less than 75 J/g as determined by DSC. SPC2 describes those polymers that are substantially crystalline in the undeformed state. Further crystallization may also occur in the presence of the crystalline polymer such as FPC. These polymers have a melting point of less than 115° C. or preferably less than 100° C. and preferably have a heat of fusion of less than 75 J/g as determined by DSC.

SUMMARY OF THE INVENTION

The present invention is directed to blends with heterophase morphology formed by blending a FPC which is a predominately crystalline stereoregular polypropylene with a SPC which is a crystallizable copolymer of a C₂, C₄-C₂₀ α-olefin (preferably ethylene) and propylene . Optional components of the blend are SPC2, a crystallizable copolymer of a C₂, C₄-C₂₀ α-olefin (preferably ethylene), and process oil. Other optional components are fillers, colorants, antioxidants, nucleators and flow improvers.

The FPC melts higher than 110° C. and preferably higher than 115° C. and more preferably higher than 130° C. and preferably has a heat of fusion of at least 75 J/g, as determined by DSC analysis. The crystalline polypropylene can be either homopolymer or copolymers with other alpha olefins. The FPC may also be comprised of commonly available isotactic polypropylene compositions referred to as impact copolymer or reactor copolymer. However these variations in the identity of the FPC are acceptable in the blend only to the extent that the FPC is within the limitations of the crystallinity and melting point indicated above. The FPC may also contain additives such as flow improvers, nucleators and antioxidants which are normally added to isotactic polypropylene to improve or retain properties. All of these polymers are referred to as the FPC.

The SPC and the SPC2, if used, have stereoregular propylene sequences long enough to crystallize. The SPC has a melting point of less than 105° C. or preferably less than 100° C. and preferably has a heat of fusion of less than 75 J/g. The SPC2 has a melting point of less than 115° C. or preferably less than 100° C. and preferably has a heat of fusion of less than 75 J/g. These stereoregular propylene sequences of SPC and SPC2 should substantially match the stereoregularity of the propylene in the first polymer. For example, if the FPC is predominately isotactic polypropylene, then the SPC, and SPC2 if used, is copolymer having isotactic propylene sequences. If the FPC is predominately syndiotactic polypropylene, then the SPC, and the SPC2 if used, is a copolymer having syndiotactic sequences. Therefore, SPC and SPC2 have similar, preferably substantially identical, tacticity to the FPC. It is believed that this matching of stereoregularity increases the compatibility of the components and results in improved adhesion at the interface of the domains of the polymers of different crystallinities in the polymer blend composition. Furthermore, good compatibility is only achieved in a narrow range of copolymer composition for the SPC. Narrow intermolecular and intramolecular compositional distribution in the copolymer is preferred. The aforementioned characteristics of the SPC, and SPC2 if used, are preferably achieved by polymerization with a chiral metallocene catalyst.

One preferable embodiment is blending isotactic polypropylene (FPC) with ethylene propylene copolymers (SPC) having about 4 wt. % to about 35 wt. % ethylene (to ensure high compatibility with the FPC). Both the FPC and the SPC have isotactic propylene sequences long enough to crystallize. Resulting blends of isotactic polypropylene with ethylene propylene copolymers according to the invention have improved properties as compared to isotactic polypropylene blends with prior art ethylene propylene rubbers.

A preferred blend comprises 1% to 95% by weight of FPC and a SPC with greater than 65% by weight propylene and preferably greater than 80% by weight propylene.

According to another embodiment, a thermoplastic polymer blend composition of the invention comprises a FPC and a SPC with added process oil. The FPC comprises isotactic polypropylene, a reactor copolymer or an impact copolymer as described above and is present in an amount of about 1% to about 95% by weight and more preferably 2% to 70% by weight of the total weight of the blend. The balance of the polymer composition consists of a mixture of the process oil and the SPC and SPC2 if used

The SPC is a random copolymer of ethylene and propylene having a melting point by DSC of 0° C. to 105° C., preferably in the range 20° C. to 90° C., more preferably in the range of 25° C. to 700° C. and an average propylene content by weight of at least 65% and more preferably at least 80%. This melting point is due to crystallizable propylene sequences, preferably of isotactic polypropylene. The SPC is made with a polymerization catalyst which forms essentially or substantially isotactic polypropylene, when all or substantially all propylene sequences in the FPC are isotactic. The SPC is statistically random in the distribution of the ethylene and propylene residues along the chain. Quantitative evaluation of the randomness of the distribution of the ethylene and propylene sequences may be obtained by consideration of the experimentally determined reactivity ratios of the second polymer component or by 13 C NMR. This is according to the procedures described in the journal article by H. Kakugo, Y Naito, K. Mizunama and T. Miyatake in Macromolecules (1982), pages 1150-1152. The SPC is made with a single sited metallocene catalyst which allows only a single statistical mode of addition of ethylene and propylene by polymerization in a well mixed, continuous feed stirred tank reactor which provides a uniform polymerization environment for growth of all of the polymer chains of the SPC.

The ratio of the FPC to the SPC of the blend composition of the present invention may vary in the range of 1:99 to 95:5 by weight and more preferably in the range 2:98 to 70:30 by weight.

According to another embodiment of the present invention, the second polymer component may contain small quantities of a non-conjugated diene to aid in the vulcanization and other chemical modification of the blend of the first polymer component and the second polymer component. The amount of diene is preferably less than 10 wt. % and preferably less than 5 wt. %. The diene may be selected from the group consisting of those which are used for the vulcanization of ethylene propylene rubbers and are preferably ethylidene norbornene, vinyl norbornene and dicyclopentadiene.

The SPC2, if used, has the same characteristics as the SPC described above. The SPC2 has a crystallinity and composition intermediate between the FPC and the SPC. In the preferred case where the SPC2 is a copolymer of ethylene and propylene while the FPC is homopolymer of propylene. The SPC2 has the same type of crystallinity of propylene as in the FPC and SPC and an ethylene content in between FPC and SPC. The addition of SPC2 to the blend leads to a better dispersion of the phases in the blend compared to blends of the similar composition which do not have any SPC2. The relative amounts of SPC and SPC2 can vary between 95:5 to 10:90 in the blend. The ratio of the FPC to the sum of SPC and SPC2 may vary in the range of 1:99 to 95:5 by weight and more preferably in the range 2:98 to 70:30 by weight

According to still a further embodiment, the invention is directed to a process for preparing thermoplastic polymer blend compositions. The process comprises: (a) polymerizing propylene or a mixture of propylene and one or more monomers selected from C₂ or C₃-C₂₀ α-olefins in the presence of a polymerization catalyst wherein a substantially isotactic propylene polymer containing at least about 90% by weight polymerized propylene is obtained; (b) polymerizing a mixture of ethylene and propylene in the presence of a chiral metallocene catalyst, wherein a copolymer of ethylene and propylene is obtained comprising up to about 35% by weight ethylene and preferably up to 20% by weight ethylene and containing isotactically crystallizable propylene sequences; and (c) blending the propylene polymer of step (a) with the copolymer of step (b) to form a blend.

The invention is directed to the formation of a blend of the components FPC, SPC and SPC2 which has a heterogeneous phase morphology consisting of domains of different crystallinities. Blends directed to improvement in the elastic recovery have a continuous phase of lower crystallinity and a dispersed phase of the higher crystallinity. The domains of the dispersed phase are small with an average minimum axis less than 5 μm. The larger axis of the dispersed phase can be as large as 100 μ. The dispersed phase consists of a crystalline mixture of FPC with some amount of SPC2 and SPC due to thermodynamic mixing of polymers. The continuous phase consists of the balance of the polymers not included in the dispersed phase. Blends directed to low flexural modulus may have in addition, a heterogeneous phase morphology with continuous phases of lower and greater crystallinity.

Commonly available propylene reactor copolymers consisting of a single phase blend of isotactic polypropylene and copolymers of propylene and ethylene are not included within the scope of the invention since they are a single phase with no prominent dispersed or continuous phases. Polypropylene blends made by a combination of a FPC and a SPC of the present invention that give a heterophase morphology in which the crystalline polymer is the continuous phase in are excluded from the invention.

The benefits of the invention are included improvement in the elastic recovery and the flexural modulus of the blend. These improvements are most apparent as a function of the 500% tensile modulus of the blend. Historically, the examples of the prior art have been able to duplicate the improvements in the blend but only for compositions with a very low 500% tensile modulus

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the morphology of a blend of this invention. Specifically, FIG. 1 shows the morphology of sample H7 in Example 6 below.

FIG. 2 shows the morphology of a blend of this invention. Specifically, FIG. 2 shows the morphology of sample K7 in Example 6 below.

FIG. 3 shows the morphology of a blend of this invention which includes SPC2. Specifically, FIG. 3 shows the morphology of sample BB7 in Example 6 below.

FIG. 4 and FIG. 5 show the stress strain elongation data for blends of this invention.

FIG. 6 shows the elastic recovery of annealed/aged blends of this invention.

FIG. 7 shows the elastic recovery of oriented blends of this invention.

FIG. 8 shows the dependence of the flexural modulus of the blend of this invention as a correlated function of the 500% tensile modulus.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

The blend compositions of the present invention generally are comprised of two components: (1) a crystalline FPC comprising isotactic polypropylene and (2) a crystallizable SPC comprising an alpha-olefin (other than propylene) and propylene copolymer. A particular embodiment of the invention contains a crystallizable SPC2 comprising an alpha-olefin (other than propylene) and propylene copolymer. A particular embodiment of the invention may comprise process oil as an additional component.

The blend also has a heterogeneous phase morphology where a more crystalline polymer mixture consisting essentially of all the FPC and some of the SPC and SPC2 is dispersed in domains in a continuous phase of a less crystalline polymer mixture containing the balance of the blend. The size of the dispersed domains is small and the morphology is stable in the absence of a compatibilizer. Preferably, compositions of the invention are free of, or substantially free of, compatibilizers.

The First Polymer Component (FPC)

In accordance with the present invention, the FPC component i.e., the polypropylene polymer component may be homopolypropylene, or copolymers of propylene, or some mixtures thereof. The FPC has the following characteristics.

(A) The polypropylene of the present invention is predominately crystalline, i.e., it has a melting point generally greater than about 110° C., preferably greater than about 115° C., and most preferably greater than about 130° C. Preferably, it has a heat of fusion greater than 75 J/g.

(B) The polypropylene can vary widely in composition. For example, substantially isotactic polypropylene homopolymer or propylene copolymer containing equal to or less than about 10 weight percent of other monomer, i.e., at least about 90% by weight propylene can be used. Further, the polypropylene can be present in the form of a graft or block copolymer, in which the blocks of polypropylene have substantially the same stereoregularity as the propylene-alpha-olefin copolymer, so long as the graft or block copolymer has a sharp melting point above about 110° C., preferably above 115° C., and more preferably above 130° C., characteristic of the stereoregular propylene sequences. The propylene polymer component may be a combination of homopolypropylene, and/or random, and/or block copolymers as described herein. When the above propylene polymer component is a random copolymer, the percentage of the copolymerized alpha-olefin in the copolymer is, in general, up to about 9% by weight, preferably about 2% to about 8% by weight, most preferably about 2% to about 6% by weight. The preferred alpha-olefins contain 2 or from 4 to about 12 carbon atoms. The most preferred alpha-olefin is ethylene. One or two or more alpha-olefins can be copolymerized with propylene.

Exemplary alpha-olefins may be selected from the group consisting of ethylene; butene-1; pentene-1,2-methylpentene-1,3-methylbutene-1; hexene-1,3-methylpentene-1,4-methylpentene-1,3,3-dimethylbutene-1; heptane-1; hexene-1,3-methylhexene-1; dimethylpentene-1 trimethylbutene-1; ethylpentene-1; octene-1; methylpentene-1; dimethylhexene-1; trimethylpentene-1; ethylhexene-1; methylethylpentene-1; diethylbutene-1; propylpentane-1; decene-1; methylnonene-1; nonene-1; dimethyloctene-1; trimethylheptene-1; ethyloctene-1; methylethylbutene-1; diethylhexene-1; dodecene-1 and hexadodecene-1.

(C) The molecular weight of the FPC can be between 10,000 to 5,000,000 with a polydispersity index (PDI) between 1.5 to 40.0

(D) The thermoplastic polymer blend compositions of the present invention may comprise from about 1% to about 95% by weight of FPC. According to a preferred embodiment, the thermoplastic polymer blend composition of the present invention may comprise from about 2% to about 70% by weight of the FPC. According to the most preferred embodiment, the compositions of the present invention may comprise from about 2% to about 40% by weight of the FPC. An even more preferred embodiment of the invention contains 2% to 25% by weight of FPC in the blend.

There is no particular limitation on the method for preparing this propylene polymer component of the invention. However, in general, the polymer is a propylene homopolymer obtained by homopolymerization of propylene in a single stage or multiple stage reactor. Copolymers may be obtained by copolymerizing propylene and an alpha-olefin having 2 or from 4 to about 20 carbon atoms, preferably ethylene, in a single stage or multiple stage reactor. Polymerization methods include high pressure, slurry, gas, bulk, or solution phase, or a combination thereof, using a traditional Ziegler-Natta catalyst or a single-site, metallocene catalyst system. The catalyst used is preferably one which has a high isospecificity. Polymerization may be carried out by a continuous or batch process and may include use of chain transfer agents, scavengers, or other such additives as deemed applicable.

The Second Polymer Component (SPC)

The SPC of the polymer blend compositions of the present invention comprises a crystallizable copolymer of propylene and another alpha-olefin having less than 10 carbon atoms, preferably ethylene. The SPC has the following characteristics:

(A) The SPC of the present invention preferably comprises a random copolymer having a narrow compositional distribution. While not meant to be limited thereby, it is believed that the narrow composition distribution of the second polymer component is important. The intermolecular composition distribution of the polymer is determined by thermal fractionation in a solvent. A typical solvent is a saturated hydrocarbon such as hexane or heptane. This thermal fractionation procedure is described below. Typically, approximately 75% by weight and more preferably 85% by weight of the polymer is soluble in one or two adjacent fractions with the balance of the polymer in immediately preceding or succeeding fractions. Each of these fractions has a composition (wt. % ethylene content) with a difference of no greater than 20 wt. % (relative) and more preferably 10 wt. % (relative) of the average wt. % ethylene content of the whole second polymer component. The second polymer component is narrow in compositional distribution if it meets the fractionation test outlined above.

(B) In all SPC, the length and distribution of stereoregular propylene sequences is consistent with the substantially random statistical copolymerization. It is well known that sequence length and distribution are related to the copolymerization reactivity ratios. By substantially random, we mean copolymer for which the product of the reactivity ratios is 2 or less. In stereoblock structures, the average length of PP sequences is greater than that of substantially random copolymers with a similar composition. Prior art polymers with stereoblock structure have a distribution of PP sequences consistent with these blocky structures rather than a random substantially statistical distribution. The reactivity ratios and sequence distribution of the polymer may be determined by C-13 NMR which locates the ethylene residues in relation to the neighboring propylene residues. To produce a copolymer with the required randomness and narrow composition distribution, it is desirable to use (1) a single sited catalyst and (2) a well-mixed, continuous flow stirred tank polymerization reactor which allows only a uniform polymerization environment for growth of substantially all of the polymer chains of the second polymer component.

(C) The SPC preferably has a single melting point. The melting point is determined by DSC. Generally, the SPC of the present invention has a melting point between about 105° C. and 0° C. Preferably, the melting point of SPC is between about 90° C. and 20° C. Most preferably, according to one embodiment of the present invention, the melting point of the SPC of the composition of the present invention is between 70° C. and 25° C.

(D) The second polymer component of the present inventive composition comprises crystallizable propylene sequences. The crystallinity of the second polymer component is, preferably, according to one embodiment, from about 1% to about 65% of homoisotactic polypropylene, preferably between 3% to 30%, as measured by the heat of fusion of annealed samples of the polymer.

(E) The molecular weight of the SPC can be between 10,000 to 5,000,000 with a polydispersity index (PDI) between 1.5 to 40.0. The second polymer component preferably has a narrow PDI between about 1.8 to about 5. It is preferred if the SPC has a Mooney Viscosity at 125° C. less than 100, more preferably less than 75 and more preferably less than 60.

(F) The low levels of crystallinity in the SPC are obtained by incorporating from about 5% to about 35% by weight alpha-olefin, preferably from about 6% to about 30% by weight alpha-olefin, and most preferably, it comprises from about 8% to about 25% by weight alpha-olefin and even more preferably between 8% to 20% by alpha-olefin. These composition ranges for the SPC are preferred to obtain the objectives of the present invention. Alpha olefins comprise one or more members of the group C₂, C₄-C₂₀ α-olefin. At alpha-olefin compositions lower than the above lower limits for the composition of the SPC, the blends of the FPC and SPC are thermoplastic and do not have the phase separated morphology required for the tensile recovery properties of the blends. At alpha-olefin compositions higher than the above higher limits for the SPC, the blends have poor tensile strength and a phase separated morphology with a coarse dispersion. It is believed, while not meant to be limited thereby, the SPC needs to have the optimum amount of polypropylene crystallinity to crystallize with the FPC for the beneficial effects of the present invention. As discussed above, the preferred alpha-olefin is ethylene.

(G) The compositions of the present invention may comprise from about 5% to about 99% by weight of the SPC and from about 30% to about 98% by weight of the SPC. Most preferably, they comprise from about 60% to about 98% and even more preferably 75% to 99% by weight of the SPC.

(H) More than one SPC may be used in a single blend with a FPC. Each of the SPC is described above and the number of SPC in this embodiment is less than three and more preferably, two. The different SPC differ in the crystallinity. For two SPC components, the SPC2 is more crystalline than the SPC. The SPC2 has, preferably, according to one embodiment, from about 20% to about 65%, and more preferably between 25% to 65% of the crystallinity of homoisotactic polypropylene as measured by the heat of fusion of annealed samples of the polymer. The SPC and the SPC2 may also differ in their molecular weight. The SPC and SPC2 differ in the alpha-olefin content consistent with the use of two SPC with different crystallinity. The preferred alpha-olefin is ethylene. It is believed that the use of SPC2 in conjunction with a blend of a FPC and a SPC acts as an interfacial agent in these blends. The resultant morphology consists of a finer dispersion of the highly crystalline component with the continuous phase of the less crystalline phase. Such a morphology leads to in the elastic recovery properties of the blends.

The second polymer component may also comprise a copolymer of atactic propylene and isotactic propylene. Such crystallizable homopolymers of propylene have been described by R. Waymouth in U.S. Pat. No. 5,594,080, which is included herein by reference. Optionally, the second component of the composition of the present invention may comprise a diene.

(I) The SPC and the SPC2, if used, have stereoregular propylene sequences long enough to crystallize. These stereoregular propylene sequences of SPC and SPC2 should match the stereoregularity of the propylene in the second polymer. For example, if the FPC is predominately isotactic polypropylene, then the SPC, and SPC2 if used, are copolymers having isotactic propylene sequences. If the FPC is predominately syndiotactic polypropylene, then the SPC, and the SPC2 if used, is a copolymer having syndiotactic sequences. It is believed that this matching of stereoregularity increases the compatibility of the components results in improved adhesion of the domains of the polymers of different crystallinities in the polymer blend composition. Furthermore, good compatibility is only achieved in a narrow range of copolymer composition for the SPC. Narrow intermolecular and intramolecular compositional distribution in the copolymer is preferred. The aforementioned characteristics of the SPC, and SPC2 if used, are preferably achieved by polymerization with a chiral metallocene catalyst.

(J) The SPC is made with a polymerization catalyst which forms essentially or substantially isotactic polypropylene when all or substantially all propylene sequences in the FPC are isotactic. Nonetheless, the polymerization catalyst used for the formation of SPC will introduce stereo- and regio-errors in the incorporation of propylene. Stereo errors are those where the propylene inserts in the chain with a tacticity that is not isotactic. A regio error in one where the propylene inserts with the methylene group or the methyldiene group adjacent to a similar group in the propylene inserted immediately prior to it. Such errors are more prevalent after the introduction of an ethylene in the SPC. Thus, the fraction of propylene in isotactic stereoregular sequences (e.g. triads or pentads) is less than 1 for SPC and decreases with increasing ethylene content of the SPC. While not wanting to be constrained by this theory, we suggest that the introduction of these errors in the introduction of propylene, particularly in the presence of increasing amounts of ethylene, are important in the use of these ethylene propylene copolymers as the SPC. Notwithstanding the presence of these errors, the SPC is statistically random in the distribution of ethylene.

(K) The SPC is made with a polymerization catalyst which forms essentially or substantially isotactic polypropylene, when all or substantially all propylene sequences in the FPC are isotactic. The SPC is statistically random in the distribution of the ethylene and propylene residues along the chain. Quantitative sequences may be obtained by consideration of the experimentally determined reactivity ratios of the second polymer component or by 13 C NMR. The SPC is made with a single sited metallocene catalyst which allows only a single statistical mode of addition of ethylene and propylene in a well-mixed, continuous monomer feed stirred tank polymerization reactor which allows only a single polymerization environment for all of the polymer chains of the SPC.

Generally, without limiting in any way the scope of the invention, one means for carrying out a process of the present invention for the production of the copolymer second polymer component is as follows: (1) liquid propylene is introduced in a stirred-tank reactor, (2) the catalyst system is introduced via nozzles in either the vapor or liquid phase, (3) feed ethylene gas is introduced either into the vapor phase of the reactor, or sparged into the liquid phase as is well known in the art, (4) the reactor contains a liquid phase composed substantially of propylene, together with dissolved alpha-olefin, preferably ethylene, and a vapor phase containing vapors of all monomers, (5) the reactor temperature and pressure may be controlled via reflux of vaporizing propylene (autorefrigeration), as well as by cooling coils, jackets, etc., (6) the polymerization rate is controlled by the concentration of catalyst, temperature, and (7) the ethylene (or other alpha-olefin) content of the polymer product is determined by the ratio of ethylene to propylene in the reactor, which is controlled by manipulating the relative feed rates of these components to the reactor.

For example, a typical polymerization process consists of a polymerization in the presence of a catalyst comprising a chiral bis (cyclopentadienyl) metal compound and either 1) a non-coordinating compatible anion activator, or 2) an alumoxane activator. An exemplary catalyst system is described in U.S. Pat. No. 5,198,401 which is herein incorporated by reference for purposes of U.S. practices. The alumoxane activator is preferably utilized in an amount to provide a molar aluminum to metallocene ratio of from about 1:1 to about 20,000:1 or more. The non-coordinating compatible anion activator is preferably utilized in an amount to provide a molar ratio of biscyclopentadienyl metal compound to non-coordinating anion of 10:1 to about 1:1. The above polymerization reaction is conducted by reacting such monomers in the presence of such catalyst system at a temperature of from about −50° C. to about 200° C. for a time of from about 1 second to about 10 hours to produce a copolymer having a weight average molecular weight of from about 5,000 or less to about 1,000,000 or more and a molecular weight distribution of from about 1.8 to about 4.5.

While the process of the present invention includes utilizing a catalyst system in the liquid phase (slurry, solution, suspension or bulk phase or combination thereof), gas phase polymerization can also be utilized. When utilized in a gas phase, slurry phase or suspension phase polymerization, the catalyst systems will preferably be supported catalyst systems. See, for example, U.S. Pat. No. 5,057,475 which is incorporated herein by reference for purposes of U.S. practice. Such catalyst systems can also include other well-known additives such as, for example, scavengers. See, for example, U.S. Pat. No. 5,153,157 which is incorporated herein by reference for purposes of U.S. practices. These processes may be employed without limitation of the type of reaction vessels and the mode of conducting the polymerization. As stated above, and while it is also true for systems utilizing a supported catalyst system, the liquid phase process comprises the steps of contacting ethylene and propylene with the catalyst system in a suitable polymerization diluent and reacting the monomers in the presence of the catalyst system for a time and at a temperature sufficient to produce an ethylene-propylene copolymer of the desired molecular weight and composition.

Process Oil

Process oil can be optimally added to the polymer blend compositions of the present invention. The addition of process oil in moderate amounts lowers the viscosity and flexibility of the blend while improving the properties of the blend at temperatures near and below 0ûC. It is believed that these benefits arise by the lowering of the Tg of the blend comprising the mixture of the FPC and the SPC. Additional benefits of adding process oil to the blend of the FPC and the SPC include improved processability and a better balance of elastic and tensile strength are anticipated.

The process oil is typically known as extender oil in the rubber application practice. The process oils can consist of (a) hydrocarbons consisting of essentially of carbon and hydrogen with traces of heteroatoms such as oxygen or (b) essentially of carbon, hydrogen and at least one heteroatom such as dioctyl phthalate, ethers and polyethers. The process oils have a boiling point to be substantially involatile at 200° C. These process oils are commonly available either as neat solids or liquids or as physically absorbed mixtures of these materials on an inert support (e.g. clays, silica) to form a free flowing powder. We believe that all forms of these process oils are equally applicable to the description and the practice of the invention.

The process oils usually include a mixture of a large number of chemical compounds which may consist of linear, acyclic but branched, cyclic and aromatic carbonaceous structures. Another family of process oils are certain low to medium molecular weight (Molecular weight (M_(n)) <10,000) organic esters and alkyl ether esters. Examples of process oils are Sunpar® 150 and 220 from The Sun Manufacturing Company of Marcus Hook, Pa., USA and Hyprene® V750 and Hyprene V1200 from Ergon, Post Office Box 1639, Jackson, Miss. 39215-1639, USA. and IRM 903 from Calumet Lubricants Co., 10234 Highway 157, Princeton, La. 71067-9172, USA. It is also anticipated that combinations of process oils each of which is described above may be used in the practice of the invention. It is important that in the selection of the process oil be compatible or miscible with the polymer blend composition of the FPC and the SPC in the melt to form a homogenous one phase blend. It is also preferred if the process oil is substantially miscible in the SPC at room temperature.

The addition of the process oils to the mixture comprising the FPC and the SPC maybe made by any of the conventional means known to the art. These include the addition of all or part of the process oil prior to recovery of the polymer as well as addition of the process oil, in whole or in part, to the polymer as a part of a compounding for the interblending of the FPC and the SPC. The compounding step may be carried out in a batch mixer such as a mill or an internal mixer such as Banbury mixer. The compounding operation may also be conducted in a continuous process such as a twin screw extruder.

The addition of certain process oils to lower the glass transition temperature of blends of isotactic polypropylene and ethylene propylene diene rubber has been described in the art by Ellul in U.S. Pat. Nos. 5,290,886 and 5,397,832. We expect these procedures are easily applicable to the FPC and SPC mixtures of the current invention.

The FPC and SPC physical mixture may include process oil in the range of from about 1 to about 200, preferably in the range of from about 2 to 50 parts by weight of process oil per hundred parts of total polymer (FPC plus SPC).

The Blend of First and Second Polymer Components

The blends of FPC and SPC and other components may be prepared by any procedure that guarantees an intimate mixture of the components. For example, the components can be combined by melt pressing the components together on a Carver press to a thickness of about 0.5 millimeter (20 mils) and a temperature of about 180° C., rolling up the resulting slab, folding the ends together, and repeating the pressing, rolling, and folding operation about 10 times. Internal mixers are particularly useful for solution or melt blending. Blending at a temperature of about 180° C. to 240° C. in a Brabender Plastograph for₌about 1 to 20 minutes has been found satisfactory. Still another method that may be used for admixing the components involves blending the polymers in a Banbury internal mixer above the flux temperature of all of the components, e.g., 180° C. for₌about 5 minutes. A complete mixture of the polymeric components is indicated by the uniformity of the morphology of the dispersion of FPC and SPC. Continuous mixing may also be used. These processes are well known in the art and include single and twin screw mixing extruders, static mixers for mixing molten polymer streams of low viscosity, impingement mixers, as well as other machines and processes, designed to disperse the first polymer component and the second polymer component in intimate contact. The polymer blends of the instant invention exhibit a remarkable combination of desirable physical properties. The incorporation of as little as 5% FPC in the SPC composed of propylene/alpha-olefin copolymers increases the melting point of the blend. In addition, the incorporation of FPC in accordance with the instant invention nearly eliminates the stickiness characteristic of the propylene/alpha-olefin copolymer alone.

The mechanism by which the desirable characteristics of the present copolymer blends are obtained is not fully understood. However, it is believed to involve a co-crystallization phenomenon between propylene sequences of similar stereoregularity in the various polymeric components, which results in a narrowing of the differences in the crystallization temperature of the blend components The combined first polymer component and second polymer component have a blend melting point closer together than would be expected on a comparison of the properties of the individual components alone. Surprisingly, some blend compositions have a single crystallization temperature and a single melting temperature, since it would be expected by those skilled in the art that the blending of two crystalline polymers would result in a double crystallization temperature as well as a double melting temperature reflecting the two polymeric components. However, the intimate blending of the polymers having the required crystallinity characteristics apparently results in a crystallization phenomenon that modifies the other physical properties of the propylene/alpha-olefin copolymer, thus measurably increasing its commercial utility and range of applications.

While the above discussion has been limited to the description of the invention in relation to having only components one and two, as will be evident to those skilled in the art, the polymer blend compositions of the present invention may comprise other additives. Various additives may be present to enhance a specific property or may be present as a result of processing of the individual components. Additives which may be incorporated include, for example, fire retardants, antioxidants, plasticizers, pigments, vulcanizing or curative agents, vulcanizing or curative accelerators, cure retarders, processing aids, flame retardants, tackifying resins, and the like. These compounds may include fillers and/or reinforcing materials. These include carbon black, clay, talc, calcium carbonate, mica, silica, silicate, combinations thereof, and the like. Other additives which may be employed to enhance properties include antiblocking agents, coloring agent. Lubricants, mold release agents, nucleating agents, reinforcements, and fillers (including granular, fibrous, or powder-like) may also be employed. Nucleating agents and fillers tend to improve rigidity of the article. The list described herein is not intended to be inclusive of all types of additives which may be employed with the present invention. Upon reading this disclosure, those of skill in the art will appreciate other additives may be employed to enhance properties of the composition. As is understood by the skilled in the art, the polymer blend compositions of the present invention may be modified to adjust the characteristics of the blend as desired.

Morphology of the Blend

The morphology of the blend is shown in Transmission Electron Microscopy of the blends. In this procedure samples were exposed to vapors of 1% aqueous RuO₄ for 3 days. The RuO₄ penetrates the amorphous zones of the continuous, less crystalline phase of the polymer while the more crystalline domains composed largely of the FPC are essentially unaffected. Within the continuous zone the RuO₄ stained the microzones of amorphous polymer while the lamellae of crystalline polymer are visible by contrast. The blend was cryomicrotomed at −196° C. to thin sections approximately 0.3 to 3 μm thick. Several sections were analyzed for each sample until a section was found where the crystalline domains was unstained while the continuous phase was stained to distinguish it from the dispersed phase and to observe the microstructure of the lamellae of polymer.

The blends of the current invention with good elastic recovery from tensile deformation had a microstructure with clearly dispersed microdomains of the crystalline phase. This is shown in FIG. 1. The composition and elastic recovery properties of the blend is shown as H7 in the Tables below. The domains are elongated with approximate dimensions of 0.2 μm×1 μm. FIG. 2 shows a different blend of the invention, designated as K7 in the Tables below, with the dispersed phase having dimensions of 0.6μm×2.0 μm. The addition of SPC2 to this blend is shown in the micrograph BB7 (FIG. 3) shows the reduction in the size of the dispersed phase to elongated particles having 0.2 μm for each dimension. SPC2 is therefore believed to act as an agent for reducing the size of the dispersion of the crystalline phases in the dispersed continuous phase. This is the morphological effect of adding SPC2 to the blend of a FPC and SPC.

Properties of the Blend: Elongation

The blends of the current invention have tensile elongation in excess of 700%. This elongation is determined for blends at 20 in/min according to the procedure described in ASTM D790. The data is reported in engineering units with no correction to the stress for the lateral contraction in the specimen due to tensile elongation.

The stress-strain elongation properties of the insitu and the corresponding physical blends was evaluated using dumbbell shaped sample. The samples were compression molded at 1800° C. to 2000° C. for 15 minutes at a force of 15 tons into a plaque of dimensions of 6 in×6 in. The cooled plaques were removed and the specimens were removed with a die. The stress strain evaluation of the samples was conducted on an Instron 4465 tester, made by Instron Corporation of 100 Royall Street, Canton, Mass. The digital data was collected in a file collected by the Series IX Material Testing System available from Instron Corporation and analyzed using Excel 5, a spreadsheet program available from Microsoft Corporation of Redmond, Wash.

FIG. 4 and FIG. 5 show the stress strain elongation data for blends containing one FPC and one SPC or two SPC respectively.

Properties of the Blend: Elastic Recovery

The benefit of the above invention i s that compositions comprising the FPC and the SPC optionally containing SPC2 and/or amounts of process oil can be made which have excellent elastic recovery from tensile deformation. These elastic blends have a morphology of containing a crystalline phase dispersed in the continuous crystallizable phase. The dispersed crystalline phase contains the majority of the FPC and some of the SPCs due to thermodynamic mixing while the continuous phase consists of the balance of the polymer blend. Elastic recovery from tensile deformation is a tension set from 200% extension of less than 40%, more preferably less than 25% and more preferably less than 15%.

These values of the tension set over the range of composition of the FPC and SPC are dependent on the 500% tensile modulus. Elastic recovery of the blend is judged on two criteria: (a) extensibility to 500% elongation with a measurable modulus and (b) tension set from an extension to 200% elongation. Comparative blends often cannot be extended to 500% extension for evaluation of the 500% modulus and, thus, cannot be compared to the blends of the current invention. Some comparative blends in the prior art can be extended to 500% elongation for the measurement of tensile modulus but have poor elastic recovery from a 200% extension. The elastic blends of the current invention fulfill both of these conditions. Generally for all blends the tension set deteriorates with increase in the 500% tensile modulus. Thus tension set from a 200% extension is judged relative to the tensile modulus of the blend for a 500% extension. The blends of the current invention have better elastic recovery, as indicated by low tension set, than blends of the comparative blends at comparable 500% tensile modulus. These properties are available over a wide range of composition and relative amounts of the FPC and the SPC. These compositions also have a range of tensile strength from 300 psi to 5000 psi. In the examples shown below, we show examples of numerous blends of composition of the FPC and the SPC which have the above favorable combination of properties.

In one embodiment, the composition of the invention has a tension set from 200% extension equal to or less than 0.02M+5, preferably equal to or less than 0.0108M+3, more preferably equal to or less than 0.0052M+2, wherein M is 500% modulus expressed in lbs/inch².

It is possible to generate comparative polymer blends with some aspect of the combined 500% tensile modulus and 200% tension set properties of the blends of this invention approached if the SPCs are of extremely high molecular weight and in the limit crosslinked. Such a combination would lead to blends which had very poor processing characteristics since they would tend to melt fracture. It is understood that those polymer blends are directed to easy processing materials that can be handled in conventional thermoplastics processing machinery.

Another part of the invention is that the elastic recovery referred to above can be enhanced by the thermal annealing of the polymer blends or by the orientation of articles made from these polymer blends. Thermal annealing of the polymer blend is conducted by maintaining the polymer blends or the articles made from a such a blend at temperature between room temperature to a maximum of 160° C. or more preferably to a maximum of 130° C. for a period between 5 minutes to less than 7 days. A typical annealing period is 3 days at 50° C. or 5 minutes at 100° C. The annealing time and temperature can be adjusted for any particular blend composition comprising a FPC and one or two SPC by experimentation. It is believed that during this annealing process, there is intermolecular rearrangement of the polymer chains, leading to a material with much greater recovery from tensile deformation than the unannealed material. The elastic recovery of annealed/aged blends of this invention is shown in FIG. 6.

Another part of the invention is that the mechanical properties referred to above can be enhanced by the mechanical orientation of the polymer blend. Mechanical orientation can be done by the temporary, forced extension of the polymer blend along one or more axis for a short period of time before it is allowed to relax in the absence of the extensional forces. It is believed that the mechanical orientation of the polymer leads to reorientation of the crystallizable portions of the blend of the first and the second polymer. Oriented polymer blends is conducted by maintaining the polymer blends or the articles made from a such a blend at an extension of 10% to 400% for a period of 0.1 seconds to 24 hours. A typical orientation is an extension of 200% for a momentary period at room temperature. The elastic recovery of oriented blends of this invention is shown in FIG. 7.

In one embodiment, articles can contain the composition of the invention after the composition has been oriented, and wherein the tension set from 200% extension equal to or less than 0.011M+3, preferably equal to or less than 0.0057M +2, more preferably equal to or less than 0.0035M+1, wherein M is 500% modulus expressed in lbs/inch

Annealing and orientation of the blend of the FPC and SPC lead to improvement in the tensile recovery properties of the blend. This is shown in the data in Tables below where the tension set recovery values for the blends described in the invention are described for the blends as made, after annealing and after orientation as described in the procedures above. The data show that the elastic recovery properties are enhanced.

Properties of the Blend: Flexural Modulus

The benefit of the above invention is that compositions comprising the FPC and the SPC containing optional amounts of process oil can be made which have low flexural modulus. These blends have a crystalline phase dispersed in the continuous crystallizable phase. The crystalline phase contains the majority of the FPC and some of the SPCs due to thermodynamic mixing while the continuous phase consists of the balance of the polymer blend. Low flexural, modulus is a 1% secant modulus less than 60 kpsi in/in, more preferably less than 30 kpsi in/in and more preferably less than 15 kpsi in/in These values of the flexural modulus over the range of composition of the FPC and SPC are dependent on the 500% tensile modulus. Flexural modulus of the blend is judged on two criteria: (a) extensibility to 500% elongation with a measurable modulus and (b) 1% secant flexural modulus. Comparative blends often cannot be extended to 500% extension for evaluation of the 500% modulus and thus cannot be compared to the blends of the current invention. The flexible blends of the current invention fulfill both of these conditions. Generally for all blends the flexural modulus deteriorates with increase in the 500% tensile modulus. Thus flexural modulus is judged relative to the tensile modulus of the blend for a 500% extension. The blends of the current invention have a lower flexural modulus, as indicated by low tension set, than blends of the comparative blends at comparable 500% tensile modulus. These properties are available over a wide range of composition and relative amounts of the FPC and the SPC. In the examples shown below we show examples of numerous blends of composition of the FPC and the SPC which have the above favorable combination of properties.

The dependence of the flexural modulus of the blend of this invention as a correlated function of the 500% tensile modulus is shown FIG. 8.

In one embodiment, the composition of the invention has a flexural modulus in kpsi.in/in equal to or less than 0.013M−1.3, preferably equal to or less than 0.0083M−1.6, more preferably equal to or less than 0.0062M−2.5 wherein M is 500% modulus expressed in lbs/inch².

In another embodiment, articles can contain the composition of the invention after the composition has been oriented, and wherein the flexural modulus in kpsi.in/in equal to or less than 0.013M−1.3, preferably equal to or less than 0.0083M−1.6, more preferably equal to or less than 0.0062M−2.5 wherein M is 500% modulus expressed in lbs/inch².

As used herein, Mooney Viscosity was measured as ML (1+4) at 125° C. in Mooney units according to ASTM DI 646.

The composition of Ethylene propylene copolymers, which are used as comparative examples, was measured as ethylene Wt. % according to ASTM D 3900.

The composition of the second polymer component was measured as ethylene Wt. % according to the following technique. A thin homogeneous film of the second polymer component, pressed at a temperature of about or greater than 150° C. was mounted on a Perkin Elmer PE 1760 infra red spectrophotometer. A full spectrum of the sample from 600 cm−1 to 400 cm−1 was recorded and the ethylene Wt. % of the second polymer component was calculated according to Equation 1 as follows:

 ethylene Wt. %=82.585−111.987×+30.045×²

wherein X is the ratio of the peak height at 1155 cm⁻¹ and peak height at either 722 cm⁻¹ or 732 cm⁻¹ which ever is higher.

Techniques for determining the molecular weight (Mn and Mw) and molecular weight distribution (MWD) are found in U.S. Pat. No. 4,540,753 (Cozewith, Ju and Verstrate) (which is incorporated by reference herein for purposes of U.S. practices) and references cited therein and in Macromolecules, 1988, volume 21, p 3360 (Verstrate et al) (which is herein incorporated by reference for purposes of U.S. practice) and references cited therein.

The procedure for Differential Scanning Calorimetry is described as follows. About 6 to 10 mg of a sheet of the polymer pressed at approximately 200° C. to 230° C. is removed with a punch die. This is annealed at room temperature for 240 hours. At the end of this period, the sample is placed in a Differential Scanning Calorimeter (Perkin Elmer 7 Series Thermal Analysis System) and cooled to about −50° C. to about −70° C. The sample is heated at 20° C./min to attain a final temperature of about 200° C. to about 220° C. The thermal output is recorded as the area under the melting peak of the sample which is typically peaked at about 30° C. to about 175° C. and occurs between the temperatures of about 0° C. and about 200° C. is measured in Joules as a measure of the heat of fusion. The melting point is recorded as the temperature of the greatest heat absorption within the range of melting of the sample. Under these conditions, the melting point of the second polymer component and the heat of fusion is lower than the first polymer component as outlined in the description above.

Composition distribution of the second polymer component was measured by the thermal fractionation as described below. About 30 gms of the second polymer component was cut into small cubes about ⅛″ on the side. This is introduced into a thick walled glass bottle closed with screw cap along with 50 mg of Irganox 1076, an antioxidant commercially available from Ciba—Geigy Corporation. Then, 425 ml of hexane (a principal mixture of normal and isomers) is added to the contents of the bottle and the sealed bottle is maintained at about 23° C. for 24 hours. At the end of this period, the solution is decanted and the residue is treated with additional hexane for an additional 24 hours. At the end of this period, the two hexane solutions are combined and evaporated to yield a residue of the polymer soluble at 23° C. To the residue is added sufficient hexane to bring the volume to 425 ml and the bottle is maintained at about 31° C. for 24 hours in a covered circulating water bath. The soluble polymer is decanted and the additional amount of hexane is added for another 24 hours at about 31° C. prior to decanting. In this manner, fractions of the second polymer component soluble at 40° C., 48° C., 55° C. and 62° C. are obtained at temperature increases of approximately 8° C. between stages. Further, increases in temperature to 95° C. can be accommodated, if heptane, instead of hexane, is used as the solvent for all temperatures above about 60° C. The soluble polymers are dried, weighed and analyzed for composition, as wt. % ethylene content, by the IR technique described above. Soluble fractions obtained in the adjacent temperature increases are the adjacent fractions in the specification above.

Comparative data was obtained with EPR which is Vistalon 457, sold by the Exxon Chemical Company, Houston Tex.

Blends were made by mixing a total of 72 g of all components, including the first polymer component, the second polymer component, the optional amounts of process oil and other ingredients in a Brabender intensive mixture for 3 minutes at a temperature controlled to be within 185° C. and 220° C. High shear roller blades were used for the mixing and approximately 0.4 g of Irganox-1076, an antioxidant available from the Novartis Corporation, was added to the blend. At the end of the mixing, the mixture was removed and pressed out into a 6″×6″ mold into a pad 025″ thick at 215° C. for 3 to 5 minutes. At the end of this period, the pad was cooled and removed and allowed to anneal for 1 day. Test specimens of the required dumbbell geometry were removed from this pad and evaluated on an Instron 4465 tester equipped with Instron Series IX Software for Windows to produce the mechanical deformation data. The Instron Tester and associated equipment is available form The Instron Corporation in Canton, Mass. The testing was done at a travel rate of 20″/min and all data is reported in engineering stress and strain term with values of the stress uncorrected for the contraction in the cross section of the sample being tested.

Samples were aged by allowing them to stand at room temperature prior to testing. Samples were aged for 5, 10, 15, 20 and 25 days prior to testing on the Instron. Significant difference in the tensile strength and tension set were observed between samples aged 1 days versus those aged for 5 or more days. There was no experimental difference between samples aged 5 days or longer.

Samples were oriented by momentarily extending them to 200% extension at room temperature. These oriented samples were retested under tensile testing conditions outlined above. Tension set was determined on the samples of the blend which has been extended on the Instron tester to 200% extension and then allowed to relax. The samples were removed and the length (L2) of the deformation zone, between the grips on the Instron tester, was measured after 10 minutes. The original distance between the rips was the original length (L1) of the deformation zone. The tension set (TSet) is given by the formula

Tset=100*(L2-L1)/L1

Flexural modulus was determined for samples of the blend by ASTM procedure D790 at room temperature.

The invention, while not meant to be limited thereby, is further illustrated by the following specific examples:

EXAMPLES Example 1 Ethylene/Propylene Copolymerization to Form the Second Polymer Component

Continuous Polymerization of the SPC was conducted in a 9 liter Continuous Flow Stirred Tank Reactor using hexane as the solvent. The liquid full reactor had a residence time of 9 minutes and the pressure was maintained at 700 kpa. A mixed feed of Hexane, ethylene and propylene was pre-chilled to approximately—30° C. to remove the heat of polymerization, before entering the reactor. Solution of catalyst/activator in Toluene and the scavenger in hexane were separately and continuously admitted into the reactor to initiate the polymerization. The reactor temperature was maintained between 35 and 50° C., depending on the target molecular weight. The feed temperature was varied, depending on the polymerization rate to maintain a constant reactor temperature. The polymerization rate was varied from about 0.5 Kg/hr to about 4 Kg/hr.

Hexane at 30 Kg/hr was mixed with ethylene at 717 g/hr and propylene at 5.14 Kg/hr and fed to the reactor. The polymerization catalyst, dimethyl silyl bridged bis-indenyl Hafnium dimethyl activated 1:1 molar ratio with N′, N′-Dimethyl anilinium-tetrakis(pentafluorophenyl)borate was introduced at the rate of at 0.0135 g/hr. A dilute solution of triisobutyl aluminum was introduced into the reactor as a scavenger of catalyst terminators: a rate of approximately 111 mole of scavenger per mole of catalyst was adequate for this polymerization. After five residence times of steady polymerization, a representative sample of the polymer produced in this polymerization was collected. The solution of the polymer was withdrawn from the top, and then steam distilled to isolate the polymer. The polymerization rate was measured at 3.7 Kg/hr. The polymer produced in this polymerization had an ethylene content of 14%, ML (1+4) 125° C. of 13.1 and had isotactic propylene sequences.

Variations in the composition of the polymer were obtained principally by changing the ratio of ethylene to propylene. Molecular weight of the polymer was varied by either changing the reactor temperature or by changing the ratio of total monomer feed rate to the polymerization rate. Dienes for terpolymerization were added to the mixed feed stream entering the reactor by preparing the diene in a hexane solution and metering it in the required volumetric amount.

Example 2 Comparative Ethylene/propylene Polymerization Where the Propylene Residues are Atactic

Polymerizations were conducted in a 1 liter thermostated continuous feed stirred tank reactor using hexane as the solvent. The polymerization reactor was full of liquid. The residence time in the reactor was typically 7-9 minutes and the pressure was maintained at 400 kpa. Hexane, ethene and propene were metered into a single stream and cooled before introduction into the bottom of the reactor.

Solutions of all reactants and polymerization catalysts were introduced continuously into the reactor to initiate the exothermic polymerization. Temperature of the reactor. was maintained at 45° C. by changing the temperature of the hexane feed and by using cooling water in the external reactor jacket. For a typical polymerization, the temperature of feed was about—10° C. Ethene was introduced at the rate of 45 gms/min and propene was introduced at the rate of 310 gms/min. The polymerization catalyst, dimethyl silyl bridged (tetramethylcyclopentadienyl) cyclododecylamido titanium dimethyl activated 1:1 molar ratio with N′, N′-Dimethyl anilinium-tetrakis(pentafluorophenyl)borate was introduced at the rate of 0.002780 gms/hr. A dilute solution of triisobutyl aluminum was introduced into the reactor as a scavenger of catalyst terminators: a rate of approximately 36.8 mole per mole of catalyst was adequate for this polymerization. After five residence times of steady polymerization, a representative sample of the polymer produced in this polymerization was collected. The solution of the polymer was withdrawn from the top, and then steam distilled to isolate the polymer. The rate of formation of the polymer was 258 gms/hr. The polymer produced in this polymerization had an ethylene content of 14.1 wt. %, ML@125 (1+4) of 95.4.

Variations in the composition of the polymer were obtained principally by changing the ratio of ethene to propene. Molecular weight of the polymer could be increased by a greater amount of ethene and propene compared to the amount of the polymerization catalyst. These polymers are described as aePP in the Tables below.

Example 3 Analysis and Solubility of Several Second Polymer Components

In the manner described in Example 1 above, several second polymer components of the above specification were synthesized. These are described in the table below. Table 1 describes the results of the GPC, composition, ML and DSC analysis for the polymers.

TABLE 1 Analysis of the second polymer component and the comparative polymers Melting (MW) Ethylene Heat of Point by ML (1 + (Mn) by by wt. % fusion DSC 4) @ 1 SPC GPC GPC by IR J/g (° C.) 25° C. SPC-1 102000 248900 7.3 71.9 84.7 14   SPC-2  9.4 30.2 65.2 27.8 SPC-3 124700 265900 11.6 17.1 43.0 23.9 SPC-4 12.8 16.4 42.5 SPC-5 14.7 13.2 47.8 38.4 SPC-6 121900 318900 16.4  7.8 40.3 33.1 SPC-7 17.8  5.3 39.5 Com- parative Polymers EPR 47.8 not not 40   detected detected AePP 11.7 not not 23   detected detected

Table 2 describes the solubility of the second polymer component

TABLE 2 Solubility of fractions of the second polymer component. Sum of the fractions add up to slightly more than 100 due to imperfect drying of the polymer fractions. Wt. % Wt. % Wt. % Wt. % soluble at soluble at soluble at soluble at SPC 23° C. 31° C. 40° C. 48° C. SPC-1  1.0  2.9 28.3 68.5 SPC-3  6.5 95.7 SPC-6  51.6 52.3  2.6 SPC-5  36.5 64.2 Comparative Polymers EPR 101.7 AePP 100.5

Table 3 describes the composition of the fractions of the second polymer component obtained in Table 2. Only fractions which have more than 4% of the total mass of the polymer have been analyzed for composition.

TABLE 3 Composition of fractions of the second polymer component obtained in Table 2. The experimental inaccuracy in determination of the ethylene content is believed to about 0.4 wt. % absolute. Composition: Wt. % ethylene in fraction soluble soluble soluble soluble soluble SPC at 23° C. at 31° C. at 40° C. at 48° C. at 56° C. SPC-1 8.0 7.6 SPC-3 12.0 11.2 SPC-6 16.8 16.5 SPC-5 14.9 14.6 Comparative EPR 46.8 Atactic ePP 11.8

Example 4

Blends were made in all composition of Table 4 according to the procedure described above.

TABLE 4 Flexural Modulus, Tensile Modulus and Tension set for Binary Blends of one FPC and SPC as molded Flexural modulus Wt % ML of C2 Wt. % 500% Modulus 100% Modulus (MPa Sample SPC1 SPC1 of SPC1 (psi) (MPa) (psi) (MPa) (kpsi in/in) cm/cm) F6 66.7 11.5 12.4 1778 12.26 1168 8.05 F7 77.8 11.5 12.4 1442 9.94 813 5.61 F8 88.9 11.5 12.4 1077 7.43 575 3.96 F9 100 11.5 12.4 971 6.69 471 3.25 G6 66.7 18.3 12.1 1800 12.41 1138 7.85 G7 77.8 18.3 12.1 1446 9.97 741 5.11 G8 88.9 18.3 12.1 1089 7.51 538 3.71 G9 100 18.3 12.1 979 6.75 472 3.25 H6 66.7 25.3 12.0 1969 13.58 1216 8.38 18.1 0.12 H7 77.8 25.3 12.0 1591 10.97 879 6.06 10.1 0.07 H8 88.9 25.3 12.0 1254 8.65 664 4.58 5.5 0.04 H9 100 25.3 12.0 1127 7.77 552 3.81 3.8 0.03 J6 66.7 39.7 13.4 1495 10.31 977 6.74 J7 77.8 39.7 13.4 1394 9.61 754 5.20 J8 88.9 39.7 13.4 904 6.23 452 3.12 J9 100 39.7 13.4 751 5.18 320 2.21 K5 55.6 28.9 14.8 1720 11.86 1297 8.94 23.1 0.16 K6 66.7 28.9 14.8 1471 10.14 990 6.83 7.7 0.05 K7 77.8 28.9 14.8 1251 8.63 621 4.28 3.9 0.03 K8 88.9 28.9 14.8 763 5.26 306 2.11 1.8 0.01 K9 100 28.9 14.8 387 2.67 200 1.38 1.3 0.01 L6 66.7 33.1 16.4 1133 7.81 613 4.23 L7 77.8 33.1 16.4 704 4.85 293 2.02 L8 88.9 33.1 16.4 573 3.95 187 1.29 L9 100 33.1 16.4 91 0.63 96 0.66 M6 66.7 25.6 17 996 6.87 597 4.12 4.2 0.03 M7 77.8 25.6 17 698 4.81 298 2.05 1.8 0.01 M8 88.9 25.6 17 336 2.32 185 1.28 1.0 0.01 M9 100 25.6 17 129 0.89 135 0.93 0.8 0.01 N8 88.9 34.5 11.1 1506 10.38 851 5.87 N9 100 34.5 11.1 1412 9.74 675 4.65 P8 88.9 16.4 10.8 1405 9.69 805 5.55 7.4 0.05 P9 100 16.4 10.8 1268 8.74 641 4.42 5.7 0.04

In this example blends of a First Polymeric Component, Escorene 4292, a homoisotactic polypropylene available from Exxon Chemical Co., Houston Tex. and one Second Polymeric component (identified as SPC1 in Table 4) were made using the procedure as described above The blends were made in a different composition range as shown by the table above. All of the compositions are within have the properties of this invention. Properties of the blend were measured as molded.

TABLE 5 Flexural Modulus, Tensile Modulus and Tension set for Binary Blends of one FPC and two SPC as molded Wt % ML of C2 Wt. % Wt. % 500% Modulus 100% Modulus Flexural modulus Sample SPC1 SPC1 of SPC1 SPC2 (psi) (MPa) (psi) (Mpa) (kpsi in/in) (MPa cm/cm) AA4 44.4 31.2 13.4 27.8 1833 12.64 1096 7.56 16.6 0.11 AA5 55.6 31.2 13.4 22.2 1571 10.83 909 6.27 11.3 0.08 AA6 66.7 31.2 13.4 16.7 1342 9.25 748 5.16 7.9 0.05 AA7 77.8 31.2 13.4 11.1 1077 7.43 524 3.61 4.7 0.03 AA8 88.9 31.2 13.4 5.56 872 6.01 385 2.65 3.4 0.02 AA9 100 31.2 13.4 0 751 5.18 320 2.21 BB4 44.4 38.4 14.7 27.8 1791 12.35 1154 7.96 17.4 0.12 BB5 55.6 38.4 14.7 22.2 1543 10.64 798 5.50 13.8 0.10 BB6 66.7 38.4 14.7 16.7 1187 8.18 548 3.78 4.8 0.03 BB7 77.8 38.4 14.7 11.1 920 6.34 379 2.61 2.9 0.02 BB8 88.9 38.4 14.7 5.56 697 4.81 386 2.66 1.9 0.01 BB9 100 38.4 14.7 0 387 2.67 200 1.38 CC5 55.6 24.9 12.1 22.2 1619 11.16 970 6.69 17.4 0.12 CC6 66.7 24.9 12.1 16.7 1504 10.37 849 5.85 12.1 0.08 CC7 77.8 24.9 12.1 11.1 1296 8.94 690 4.76 8.7 0.06 CC8 88.9 24.9 12.1 5.56 1 152 7.94 581 4.01 5.8 0.04 CC9 100 24.9 12.1 0 1051 7.25 481 3.32 4.6 0.03 EE5 55.6 31.2 13.4 13.32 2019 13.92 1303 8.98 EE6 66.7 31.2 13.4 10.02 1581 10.90 878 6.05 EE7 77.8 31.2 13.4 6.66 1398 9.64 643 4.43 EE8 88.9 31.2 13.4 3.33 1064 7.34 457 3.15 EE9 100 31.2 13.4 0 871 6.01 381 2.63 FF5 55.6 38.4 14.7 13.32 1830 12.62 1214 8.37 22.0 0.15 FF6 66.7 38.4 14.7 10.02 1612 11.11 847 5.84 8.4 0.06 FF7 77.8 38.4 14.7 6.66 1168 8.05 470 3.24 4.1 0.03 FF8 88.9 38.4 14.7 3.33 921 6.35 369 2.54 2.5 0.02 FF9 100 38.4 14.7 0 579 3.99 264 1.82 2.0 0.01 DD4 44.4 23.4 16.8 27.8 1640 11.31 1053 7.26 13.2 0.09 DD5 55.6 23.4 16.8 22.2 1424 9.82 708 4.88 6.2 0.04 DD6 66.7 23.4 16.8 16.7 1178 8.12 437 3.01 2.5 0.02 DD7 77.8 23.4 16.8 11.1 849 5.85 270 1.86 1.4 0.01 DD8 88.9 23.4 16.1 5.56 535 3.69 199 1.37 1.1 0.01 DD9 100 23.4 16.1 0 318 2.19 135 0.93 GG6 66.7 24.9 12.1 10.02 1751 12.07 975 6.72 GG7 77.8 24.9 12.1 6.66 1563 10.78 798 5.50 GG8 88.9 24.9 12.1 3.33 1279 8.82 624 4.30 GG9 100 24.9 12.1 0 1129 7.78 552 3.81 HH5 55.6 23.4 16.8 13.32 1385 9.55 964 6.65 13.1 0.09 HH6 66.7 23.4 16.8 10.02 1005 6.93 501 3.45 4.0 0.03 HH7 77.8 23.4 16.8 6.66 531 3.66 251 1.73 1.9 0.01 HH8 88.9 23.4 16.8 3.33 318 2.19 184 1.27 1.1 0.01 HH9 100 23.4 16.8 0 129 0.89 135 0.93 JJ6 66.7 31.2 13.4 3.33 1569 10.82 889 6.13 JJ7 77.8 31.2 13.4 2.22 1303 8.98 603 4.16 JJ8 88.9 3i.2 13.4 1.11 1007 6.94 417 2.88 JJ9 100 31.2 13.4 0 753 5.19 320 2.21 KK5 55.6 38.4 14.7 4.44 1943 13.40 1316 9.07 KK6 66.7 38.4 14.7 3.33 1666 11.49 871 6.01 KK7 77.8 38.4 14.7 2.22 1295 8.93 507 3.50 KK8 88.9 38.4 14.7 1.11 976 6.73 383 2.64 KK9 100 38.4 14.7 0 387 2.67 200 1.38 LL6 66.7 24.9 12.1 3.33 1944 13.40 1121 7.73 LL7 77.8 24.9 12.1 2.22 1599 11.02 854 5.89 LL8 88.9 24.9 12.1 1.11 1259 8.68 638 4.40 LL9 100 24.9 12.1 0 1127 7.77 552 3.81

In this example blends of a First Polymeric Component, Escorene 4292, a homoisotactic polypropylene available from Exxon Chemical Co., Houston Tex. and two Second Polymeric component (identified as SPC1 and SPC2 in Table 5) were made using the procedure as described above. The SPC2 has a ML(1+4)@125 of 14 and an ethylene content of 7.3 wt. %. The composition and the ML of the SPC1 are indicated in the Table for the various SPC1 used. The blends were made in a different composition range as shown by the table above. All of the compositions are within have the properties of this invention. Properties of the blend were measured as molded.

Example 6

TABLE 6 Hysteresis and Tension set for Binary Blends of one FPC and one SPC and Ternary Blend of one FPC and two SPC described in Table 4 and 5 as (1) new, (2) after annealing at room temperature for 21 days and (3) after momentary orientation to 200%. 200% Hysterisis Set Tension Set % Sample New Annealed Oriented New Annealed Oriented F6 55 56 31 28 27  6 F7 35 29 16 19 16 6 F8 20 24 15 16  9 6 F9 18 16  6  9  3 3 H6 65 64 31 34 31 13  H7 38 36 16 19 19 6 H8 33 25 16 16 13 3 H9 21 21 13 14  6 2 M5 91 71 54 42 31 16  M6 65 48 41 25  9 9 M7 38 28 29  9  6 3 M8 33 24 23  6  3 3 M9 32 19 20  9  3 2 N8 52 13 13 31  6 6 N9 57 33 32 38 16 19  P7 57 54 57 38 27 13  P8 39 34 34 25 22 10  P9 33 23 23 25 16 6 G6 60 56 31 28 25 13  G7 33 31 16 19 16 6 G8 24 28  8 13  9 3 G9 12 13  6  8  9 3 J6 47 21 21 19  9 9 J7 31 24 16 13 11 6 J8 18 13  7 13  9 6 J9 15  9  3  6  6 2 K5 71 79 48 34 41 16  K6 48 33 25 52 16 9 K7 19 15 11  9  9 2 K8 14 13  1  6  6 0 K9 16  8  6  5  3 0 L6 60 35 21 25 13 8 L7 39 20 14  9  3 5 L8 31 15  5  8  8 3 L9 31 31  9  9  0 3 AA4 65 54 43 33 28 14  AA5 40 39 20 25 19 8 AA6 27 31 16 22 16 5 AA7 19 19 11 16 13 5 AA8 17 14 13 13  9 2 BB4 53 56 35 28 28 9 BB5 37 36 19 19 19 6 BB6 23 15 16 14  9 6 BB7 14 20  5 11  6 5 BB8 14 18 10  9  6 3 CC5 58 49 30 34 25 16  CC6 43 41 20 22 16 8 CC7 29 24 15 19 13 6 CC8 28 20 11 17  9 6 EE5 60 56 60 31 42 11  EE6 35 26 35 17 14 6 EE7 21 14 21 13  9 5 EE8 16 14 16  9  6 2 FF4 88 81 64 50 33 25  FF5 52 48 31 30 23 13  FF6 23 23 15 13  9 6 FF7 19 11  5  9  6 3 FF8  9  8  5  6  3 2 DD4 65 56 39 31 23 6 DD5 34 34 26 16 25 6 DD6 28 23 20 11 17 3 DD7 24 23 20  9 13 3 DD8 28 24 15  6  9 0 G66 43 43 43 25 25 9 GG7 28 28 28 19 16 9 GG8 22 22 22 16 13 6 HH4 79 79 54 45 41 19  HH5 64 64 39 34 28 11  HH6 38 34 26 16 11 5 HH7 28 30 21  9  6 2 HH8 26 25 15  6  3 0 JJ5 73 73 73 41 38 19  JJ6 35 35 35 19 16 8 JJ7 17 17 17 13  9 5 JJ8 13 13 13  9  6 5 KK5 56 64 39 31 28 11 KK6 30 26 19 17 13 5 KK7 18 11  9  9  6 2 KK8 11 12  6  9  6 2 LL6 60 60 60 34 31 13  LL7 32 32 32 19 16 8 LL8 26 26 26 16 13 6

Example 7

Blends were made in all composition of Table 7 according to the procedure described above.

TABLE 7 Blends where the FPC is a reactor copolymer and the SPC are described below Wt % Wt % 500% Modulus 100% Modulus Sample SPC1 FPC (psi) (MPa) (psi) (MPa) 2AA1 44.4 44.4 2AA2 38.8 38.8 2AA3 33.3 33.3 2AA4 27.8 27.8 1302 8.98 919 6.34 2AA5 22.2 22.2 1194 8.23 794 5.47 2AA6 16.7 16.7 1013 6.98 604 4.16 2AA7 11.1 11.1  857 5.91 486 3.35 2AA8 5.55 5.55  690 4.76 353 2.43 2BB1 27 62 2BB2 23 54 2BB3 20 47 2BB4 17 39 1311 9.04 994 6.85 2BB5 13 31  125 0.86 821 5.66 2BB6 10 23 1006 6.94 591 4.07 2BB7 7 16  823 5.67 438 3.02 2BB8 3 8  657 4.53 338 2.33

In this example blends of a First Polymeric Component, Escorene 9272, a reactor copolymer available from Exxon Chemical Co., Houston Tex. having an ethylene content of 5 wt % and 2.9 MFR and two Second Polymeric component (identified as SPC1 and SPC2 in Table 7) were made using the procedure as described above. The SPC1 has a ML(1+4)@125 of 11 and an ethylene content of 14.5 wt %. The SPC2 has a ML(1+4)@125 of 21 and an ethylene content of 5.8 wt %. The blends were made in a different composition range as shown by the table above. All of the compositions are within have the properties of this invention. Properties of the blend were measured as molded.

Example 8

TABLE 8 Hysteresis and Tension set for Binary Blends of one FPC and one SPC and Ternary Blend of one FPC and two SPC described in Table 7 as (1) new, (2) after annealing at room temperature for 21 days and (3) after momentary orientation to 200%. 200% Hysterisis Set Tension Set % Sample New Annealed Oriented New Annealed Oriented 2AA4 63 63 33 29 37  6 2AA5 39 39 28 20 22   9. 2AA6 31 29 15 17 16  3 2AA7 26 26 11 11 12  3 2AA8 18 15  9  8  9  3 2BB4 63 71 39 40 34 18 2BB5 44 43 28 37 19  12. 2BB6 26 31 15 12  12.  4 2BB7 19 20 11  9 11  3 2BB8 18 18 10  9 11  3

Example 9

Blends were made in all composition of Table 7 according to the procedure described above.

TABLE 9 Blends where the FPC is a reactor copolymer and the SPC are described below Wt % Wt % 500% Modulus 100% Modulus Sample SPC1 FPC (psi) (MPa) (psi) (MPa) 2CC1 44.4 44.4 2CC2 38.8 38.8 2CC3 33.3 33.3 2CC4 27.8 27.8 1524 10.51  1082  7.46 2CC5 22.2 22.2 1261 8.69 733 5.05 2CC6 16.7 16.7 1119 7.72 581 4.01 2CC7 11.1 11.1  854 5.89 411 2.83 2CC8 5.55 5.55  656 4.52 304 2.17 2DD1 27 62 2DD2 23 54 2DD3 20 47 2DD4 17 39 1647 11.36  1314  9.06 2DD5 13 31 1452 10.01  834 5.75 2DD6 10 23 1196 8.25 610 4.21 2DD7 7 16  885 6.10 388 2.68 2DD8 3 8  670 4.62 283 1.95

In this example blends of a First Polymeric Component, Escorene 7132, a impact copolymer available from Exxon Chemical Co., Houston Tex. having an ethylene content of 9 wt % and 2.0 MFR and two Second Polymeric component (identified as SPC1 and SPC2 in Table 7) were made using the procedure as described above. The SPC1 has a ML(1+4)@125 of 11 and an ethylene content of 14.5 wt %. The SPC2 has a ML(1+4)@125 of 21 and an ethylene content of 5.8 wt %. The blends were made in a different composition range as shown by the table above. All of the compositions are within have the properties of this invention.Properties of the blend were measured as molded.

Example 10

TABLE 10 Hysteresis and Tension set for Binary Blends of one FPC and one SPC and Ternary Blend of one FPC and two SPC described in Table 9 as (1) new, (2) after annealing at room temperature for 21 days and (3) after momentary orientation to 200%. 200% Hysterisis Set Tension Set % Sample New Annealed Oriented New Annealed Oriented 2CC4 66 77 39 37.5 34.375 14.0625 2CC5 44 41 28 23.4375 18.75 4.6875 2CC6 25 31 16 10.9375 9.375 3.125 2CC7 18 18 10 10.9375 9.375 3.125 2CC8 19 19 11 9.375 7.8125 1.5625 2DD4 89 89 58 53.125 34.375 25 2DD5 44 40 26 20.3125 18.75 6.25 2DD6 31 28 16 10.9375 10.9375 4.6875 2DD7 18 19  9 7.8125 7.8125 3.125 2DD8 21 19 11 4.6875 6.25 3.125

Example 11

Blends were made in all composition of Table 11 according to the procedure described above.

TABLE 11 Blends where the FPC is an isotactic homopolymer, a process oil and the SPC are described below Wt % Wt % Wt % Sunpar 500% Modulus 100% Modulus Sample SPC1 FPC 150 (psi) (MPa) (psi) (MPa) 2EE1 36 36 20 2EE2 31 31 20 1355 9.34 1130 7.79 2EE3 27 27 20 1248 8.60 945 6.52 2EE4 22 22 20 1119 7.72 749 5.16 2EE5 18 18 20 902 6.22 532 3.67 2EE6 13 13 20 690 4.76 336 2.32 2EE7 9 9 20 576 3.97 274 1.89 2EE8 4 4 20 386 2.66 176 1.21 2EE9 0 0 20 221 1.52 121 0.83 2FF1 21 50 20 2FF2 19 44 20 1552 10.70 1313 9.05 2FF3 16 37 20 1442 9.94 1113 7.67 2FF4 13 31 20 1264 8.71 831 5.73 2FF5 11 25 20 1025 7.07 569 3.92 2FF6 8 19 20 798 5.50 387 2.67 2FF7 5 12 20 605 4.17 269 1.85 2FF8 3 6 20 406 2.80 176 1.21

In this example blends of a First Polymeric Component, Escorene 4292, a isotactic homopolymer available from Exxon Chemical Co., Houston Tex. having 0.9 MFR and two Second Polymeric component (identified as SPC1 and SPC2 in Table 7) were made using the procedure as described above. The SPC1 has a ML(1+4)@125 of 11 and an ethylene content of 14.5 wt %. The SPC2 has a ML(1+4)@125 of 21 and an ethylene content of 5.8 wt %. Sunpar 150 is a process oil available from Sun Refining Company. The blends were made in a different composition range as shown by the table above. All of the compositions are within have the properties of this invention. Properties of the blend were measured as molded.

Example 12

TABLE 12 Hysteresis and Tension set for Ternary Blend of one FPC and two SPC and a process oil described in Table 11 as (1) new, (2) after annealing at room temperature for 21 days and (3) after momentary orientation to 200%. 200% Hysterisis Set Tension Set % Sample New Annealed Oriented New Annealed Oriented EE3 58 58 43 31.25 28.125 10.9375 EE4 43 46 31 21.875 21.875 7.8125 EE5 36 36 21 15.625 17.1875 4.6875 EE6 25 26 15 10.9375 12.5 4.6875 EE7 18 19 11 7.8125 10.9375 4.6875 EE8 16 18  9 4.6875 7.8125 3.125 EE9 11 13 14 1.5625 4.6875 0 FF3 76 76 53 39.0625 37.5 15.625 FF4 58 53 36 28.125 26.5625 7.8125 FF5 38 38 29 15.625 17.1875 7.8125 FF6 29 24 21 10.9375 10.9375 6.25 FF7 20 19 11 7.8125 7.8125 3.125 FF8 16 18 11 6.25 6.25 3.125

Example 12 Comparative Blends

Comparative blends of compositions similar to those of the blends of the inventive composition were made with EPR and aePP as shown in Table 1. In all cases the blends had a tensile elongation less than 500% and are not reported in either the FIGS. 6, 7 and 8.

While the illustrative embodiments of the invention have been described with particularity, it will be understood that various other modifications will be apparent to and can be readily made by those skilled in the art without departing from the spirit and scope of the invention. Accordingly, it is not intended that the scope of the claims appended hereto be limited to the examples and descriptions set forth herein but rather that the claims be construed as encompassing all the features of patentable novelty which reside in the present invention, including all features which would be treated as equivalents thereof by those skilled in the art to which the invention pertains. 

What is claimed is:
 1. An uncrosslinked blend composition comprising a dispersed phase of a crystalline polymer component in a continuous phase of a crystallizable polymer component wherein: a) the crystalline polymer component is dispersed in phases less than 3 μm×3 μm×100 μm in size, b) the blend composition has greater than 65% propylene units by weight, c) the blend comprises greater than 1% but less than 40% by weight is based on the total weight of the blend of a crystalline first polymer component and less than 99% but greater than 60% by weight based on the total weight of the blend of a crystallizable second polymer component, such crystallinity being due to stereoregular polymerized propylene units, d) both first and second polymer component contain stereoregular polymerized propylene units of identical tacticity, e) the blend has a tensile elongation greater than 650%, wherein the first polymer component is a propylene homopolymer and has a melting point by DSC equal to or above 115° C., and the second polymer component is a copolymer of the propylene units and from about 8%/ to about 25% by weight ethylene units and has a melting point equal to or less than about 100° C.
 2. The composition of claim 1 wherein an additional second polymer component, intermediate in melting point and heat of fusion between the first polymer component and the second polymer component Is added, and wherein said additional second polymer component comprises stereoregular polypropylene of similar tacticity to the first and second polymer component.
 3. The composition of claim 1 wherein the stereoregular polypropylene is isotactic polypropylene.
 4. The composition of claim 1 wherein the second polymer component has a heat of fusion less than 75 J/g.
 5. The composition of claim 1 wherein the second polymer component has a melting point by DSC between about 3020 C. and about 100° C.
 6. The composition of claim 1 wherein the second polymer component has a molecular weight distribution of about 2.0 to about 3.2.
 7. The composition of claim 1 wherein the second polymer component is made in a solution polymerization process.
 8. The composition of claim 1 wherein the first polymer component has a melting point equal to or greater than about 130° C.
 9. The composition of claim 1 additionally comprising process oil.
 10. The composition of claim 1 wherein the glass transition temperature of the blend is lower than the glass transition temperature of the second polymer component used to make the blend.
 11. The composition of claim 1 having a tension set from 200% extension equal to or less than 0.02M+5 wherein M is 500% modulus expressed in lbs/inch².
 12. The composition of claim 1 having a tension set from 200% extension equal to or less than 0.0108M+3 wherein M is 500% modulus expressed in lbs/inch².
 13. The composition of claim 1 having a tension set from 200% extension equal to or less than 0.0052M+2 wherein M is 500% modulus expressed in lbs/inch².
 14. The composition of claim 1 having a flexural modulus in kpsi.in/in equal to or less than 0.013M−1.3 wherein M is 500% modulus expressed in lbs/inch².
 15. The composition of claim 1 having a flexural modulus in kpsi.in/in equal to or less than 0.0083M−1.6 wherein M is 500% modulus expressed in lbs/inch².
 16. The composition of claim 1 having a flexural modulus in kpsi.in/in equal to or less than 0.0062M−2.5 wherein M is 500% modulus expressed in lbs/inch².
 17. The composition of claim 1 wherein said composition has been annealed.
 18. The composition of claim 1 wherein said composition has been oriented.
 19. An article of manufacture comprising the composition of claim
 18. 20. The article of claim 19 having a tension set equal to or less than 0.011M+3 wherein M is 500% modulus expressed in lbs/inch².
 21. The article of claim 19 having a tension set equal to or less than 0.0057M+2 wherein M is 500% modulus expressed in lbs/inch^(2.)
 22. The article of claim 19 having a tension set equal to or less than 0.0035M+1 wherein M is 500% modulus expressed in lbs/inch².
 23. The article of claim 19 having a flexural modulus in kpsi.in/in equal to or less than 0.013M−1.3 wherein M is 500% modulus expressed in lbs/inch².
 24. The article of claim 19 having a flexural modulus in kpsi.in/in equal to or less than 0.0083M−1.6 wherein M is 500% modulus expressed in lbs/inch².
 25. The article of claim 19 having a flexural modulus in kpsi.in/in equal to or less than 0.0062M−2.5 wherein M is 500% modulus expressed in lbs/inch².
 26. The article of claim 19 wherein said composition is annealed.
 27. An uncrosslinked blend composition comprising a dispersed phase of a crystalline polymer component in a continuous phase of a crystallizable polymer component wherein: the crystalline polymer component is dispersed in phases less than 3 μm ×3 μm×100 μm in size, b) the blend composition has greater than 65% propylene units by weight, c) the blend comprises greater than 2% but less than 22.2% by weight based on the total weight of the blend of a crystalline first polymer component and less than 98% but greater than 77.8% by weight based on the total weight of the blend of a crystallizable second polymer component, such crystallinity being due to stereoregular polymerized propylene units, d) both first and second polymer component contain stereoregular polymerized propylene units of identical tacticity, e) the blend has a tensile elongation greater than 650%, wherein the first polymer component is a propylene homopolymer and has a melting point by DSC equal to or above 115° C., and the second polymer component is a copolymer of the propylene units and from about 8% to about 25% by weight ethylene units and has a melting point equal to or less than about 100° C.
 28. The composition of claim 27 wherein an additional second polymer component, intermediate in melting point and heat of fusion between the first polymer component and the second polymer component is added, and wherein said additional second polymer component comprises stereoregular polypropylene of similar tacticity to the first and second polymer component.
 29. The composition of claim 27 wherein the stereoregular polypropylene is isotactic polypropylene.
 30. The composition of claim 27 wherein the second polymer component has a heat of fusion less than 75 J/g.
 31. The composition of claim 27 wherein the second polymer component has a melting point by DSC between about 3020 C. and about 100° C.
 32. The composition of claim 27 wherein the second polymer component has a molecular weight distribution of about 2.0 to about 3.2.
 33. The composition of claim 27 wherein the second polymer component is made in a solution polymerization process.
 34. The composition of claim 27 wherein the first polymer component has a melting point equal to or greater than about 13020 C.
 35. The composition of claim 27 additionally comprising process oil.
 36. The composition of claim 27 wherein the glass transition temperature of the blend is lower than the glass transition temperature of the second polymer component used to make the blend.
 37. The composition of claim 27 having a tension set from 200% extension equal to or less than 0.02M+5 wherein M is 500% modulus expressed in lbs/inch².
 38. The composition of claim 27 having a tension set from 200% extension equal to or less than 0.0108M+3 wherein M is 500% modulus expressed in lbs/inch².
 39. The composition of claim 27 having a tension set from 200% extension equal to or less than 0.0052M+2 wherein M is 500% modulus expressed in lbs/inch².
 40. The composition of claim 27 having a flexural modulus in kpsi.in/in equal to or less than 0.013M−1.3 wherein M is 500% modulus expressed in lbs/inch².
 41. The composition of claim 27 having a flexural modulus in kpsi.in/in equal to or less than 0.0083M−1.6 wherein M is 500% modulus expressed in lbs/inch².
 42. The composition of claim 27 having a flexural modulus in kpsi.in/in equal to or less than 0.0062M−2.5 wherein M is 500% modulus expressed in lbs/inch².
 43. The composition of claim 27 wherein said composition has been annealed.
 44. The composition of claim 27 wherein said composition has been oriented.
 45. An article of manufacture comprising the composition of claim
 27. 